Magnetsko ponašanje slojevitih halogenokuprata temeljenih na alifatskim triaminima

diplomski rad

• Naslov (engleski): Magnetic behaviour of layered halocuprates based on aliphatic triamines
• Autor: Petar Havaić
• Mentor: Damir Pajić (mentor)
• Član povjerenstva: Damir Pajić (predsjednik povjerenstva)
• Član povjerenstva: Damjan Pelc (član povjerenstva)
• Član povjerenstva: Ivan Kupčić (član povjerenstva)
• Član povjerenstva: Miroslav Požek (član povjerenstva)
• Član povjerenstva: Ivan Kokanović (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prirodoslovno-matematički fakultet; (Fizički odsjek); Zagreb
• Datum i država obrane: 2023-09-27, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Fizika

Sažetak

Fizička svojstva metalo-organskih spojeva godinama su u fokusu mnogih znanstvenih istraživanja. Halogeno-kuprati temeljenim na alifatskim triaminima su spojevi koji pripadaju skupini slojevitih perovskitnih materijala. Mjereni su spojevi tetraklorokuprata i tetrabromokuprata povezani s alifatskim triaminima koji mogu biti multiferoični. Ta četiri uzorka su: N2N3NCuCl5 i N2N2NCuCl5 te N2N3NCuBr5 i N2N2NCuBr5 (gdje 2 znači dvočlani ugljikov lanac, 3 za tročlani ugljikov lanac, dok N označuje amonijevu skupinu). U mag. sloju su halidnim mostovima spojeni ioni bakra, a među tim vezama nalaze se organski kationi, koji se vežu na njih te međusobno povezuju ravnine čineći cijelu kristalnu stukturu. Ti spojevi su dobri kandidati za pokazivanje multiferoičkog uređenja, jer imaju zanimljiva različita magnetska i električna svojstva. Ovdje smo proučavali magnetska svojstva koristeći SQUID magnetometar za istraživanje magnetskog ponašanja sitnih uzoraka u širem rasponu temperatura i magnetskih polja. Izmjerene su ovisnosti magnetizacija M(T) za nekoliko primjenjenih mag. polja te izotermne ovisnosti o mag. polju M(H), pri temperaturama od 2-50 K. Temperaturne ovisnosti magnetizacija za N2N2NCuBr5 pokazale su postojanje feromagnetskog faznog prijelaza na Curievoj temperaturi 20.5 K, dok su ostali spojevi pokazali antiferomagnetski fazni prijelaz na više različitih temperatura, nižih od spomenutog slabog feromagneta. Uzrok antiferomagnetskih uređenja je slaba interakcija susjednih feromagnetski uređenih slojeva kristalne strukture. Za te spojeve je primjećeno da se na većim jakostima polja (1000 Oe) uspostavlja feromagnetsko ponašanje.

Sažetak (engleski)

Physical properties of the metal-organic compounds have been for years been in focus of exstensive research for many years. Halo-cuprates based on the aliphatic triamines are compounds which belong to group of the layered pervoskite materials, which could be multiferroic. Measured compounds are the tetrachlorocuprates and tetrabromocuprates coupled with aliphatic triamines. These four samples are: N2N3NCuCl5, N2N2NCuCl5 and N2N3NCuBr5, N2N2NCuBr5 (Where 2 means 2 carbon chains, 3 means 3 carbon chains while N means amin group). In magnetic layer halid bridges are bonded with copper ions and between these bonds there are organic cations which bond on to them thus connencting planes which makes the whole crystal structure. Those compounds are good candidates for showing multiferroic ordering, because they have different magnetic and electric properties. Here we were investigating magnetic properties using SQUID magnetometer which is used for purpose of researching the magnetic behaviour of the small samples in a wide range of temperature and magnetic fields. Temperature dependencies of magnetisations M(T) in several magnetic fields and isothermal magnetic hysteresis M(H) at temperatures 2-50 K were measured. Temperature dependencies of magnetisation for N2N2NCuBr5 showed the existence of the ferromagnetic phase transition at Curie temperature of 20.5 K, while other compunds showed the antiferomagnetic phase transitions at different temperatures, lower than before mentioned weak ferromagnet. Cause of the antiferromagnetic ordering is weak interaction between neighbouring ferromagnetic ordered layers of crystal structure. For this compounds it has been noticed that at higher fields (1000 Oe) ferromagnetic behaviour apears.

• Ključne riječi: metalo-organski spoj; slojeviti perovskiti; magnetizacija; feromagneti; antiferomagneti; susceptibilnost; magnetska histereza; SQUID magnetometar; Curieva temperatura; međudjelovanja
• Ključne riječi (engleski): metal-organic compound; layered perovskites; magnetization; ferromagnet; antiferromagnet; susceptibility; magnetic hysteresis; SQUID magnetometer; Curie temperature; interactions
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:217:669495
• Studijski program: Naziv: Fizika i tehnika; smjerovi: Nastavnički; Smjer: Nastavnički; Vrsta studija: sveučilišni; Stupanj studija: integrirani prijediplomski i diplomski; Akademski / stručni naziv: sveučilišni magistar edukacije fizike i tehnike (univ. mag. educ. phys. et techn.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Rad dostupan nakon; Datum isteka embarga: 2025-09-27
• Datum i vrijeme pohrane: 2024-02-05 14:06:16