Sinteza i karakterizacija jodidnih kompleksa prijelaznih metala pripravljenih mehanokemijskom sintezom u šupljinama zeolita strukturnog tipa FAU

diplomski rad

• Naslov (engleski): Synthesis and characterization of transition metal iodide complexes prepared by mechanochemical synthesys within the voids of FAU-type zeolite material
• Autor: Emilija Petrović Hađar
• Mentor: Ana Palčić (mentor)
• Član povjerenstva: Vladimir Stilinović (predsjednik povjerenstva)
• Član povjerenstva: Gordan Horvat (član povjerenstva)
• Član povjerenstva: Ivan Nemet (član povjerenstva)
• Član povjerenstva: Vinko Nemec (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prirodoslovno-matematički fakultet; (Kemijski odsjek); Zagreb
• Datum i država obrane: 2024-10-02, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija

Sažetak

Zeoliti su mikroporozni kristalni alumosilikatni materijali uređene strukture koju karakteriziraju šupljine i kanali određenih dimenzija te svojstva poput ionske izmjene i velikog apsorpcijskog kapaciteta. Svoju primjenu pronalaze kao katalizatori, apsorbensi, pročišćivači i dr. U ovom radu korišten je zeolit strukturnog tipa FAU kojeg karakteriziraju velike šupljine (promjer šupljina do 11,2 Å) i stabilnost pri visokim temperaturama. Provedena je mehanokemijska poslijesintetska modifikacija zeolita strukturnog tipa FAU kationima prijelaznih metala (željeza(II), kobalta(II), nikla(II) i bakra(II)) nakon čega je uslijedilo mljevenje s jodom ili kalijevim jodidom. Na taj način sintetizirano je osam različitih jodidnih kompleksa prijelaznih metala unutar šupljina zeolita strukturnog tipa FAU. Kompleksi su identificirani usporedbom simuliranih far-IR spektara, korištenjem hibridnog DFT funkcionala tipa WB97XD, sa snimljenim spektrima. Naposljetku, uzorci su izloženi korozivnim atmosferama dušikova dioksida i klorovodika te je pokazana uzajamna stabilizacija zeolita i kompleksa u ovakvim uvjetima.

Sažetak (engleski)

Zeolites are microporous crystalline alumosilicate materials with an organized structure characterized by cavities and channels of specific dimensions, and properties like ion-exchange and high absorption capacity. They are used as catalysts, absorbents, and purifiers, among others. In this work, FAU-type zeolite, which is characterized by large cavities (cavity diameters up to 11.2 Å) and stability at high temperatures, was used. A mechanochemical post- synthetic modification of the FAU-type zeolite with transition metal cations (iron(II), cobalt(II), nickel(II), and copper(II)) was carried out, followed by grinding with iodine or potassium iodide. The result was eight different iodide complexes of transition metals synthesized within cavities of the FAU-type zeolite. The complexes were identified by comparing simulated far- IR spectra, by using the hybrid DFT functional WB97XD, and experimental spectra. Finally, the samples were exposed to corrosive atmospheres of nitrogen dioxide and hydrogen chloride, demonstrating the mutual stabilization of the zeolite and complexes under such conditions.

• Ključne riječi: apsorpcija; jodidni kompleksi; mehanokemija; poslijesintetska modifikacija; zeolit strukturnog tipa FAU
• Ključne riječi (engleski): absorption; FAU-type zeolite; iodide complexes; mechanochemistry; post-synthetic modification
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:217:099943
• Projekt: Šifra: UIP-2019-04-4977; Naziv: Zeoliti s malim šupljinama modificirani bakrom pogodni za primjenu u zaštiti okoliša; Naziv: Copper-modified Small-pore Zeolites Suitable for Environmental Applications; Kratica: SMALLPORE; Voditelj: Ana Palčić; Pravna nadležnost: Hrvatska; Financijer: Hrvatska zaklada za znanost; Linija financiranja: Installation Research Projects
• Studijski program: Naziv: Kemija; smjerovi: Istraživački; Smjer: Istraživački; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: sveučilišni/a magistar/magistra kemije (univ. mag. chem.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Rad dostupan nakon; Datum isteka embarga: 2025-10-02
• Datum i vrijeme pohrane: 2024-10-23 12:30:24