Prikladnost nanočestica zlata za analizu sterigmatocistina SERS spektroskopijom

diplomski rad

• Naslov (engleski): Suitability of gold nanoparticles for sterigmatocystin analysis by SERS spectroscopy
• Autor: Petra Petrović
• Mentor: Snežana Miljanić (mentor)
• Član povjerenstva: Snežana Miljanić (predsjednik povjerenstva)
• Član povjerenstva: Željka Soldin (član povjerenstva)
• Član povjerenstva: Đani Škalamera (član povjerenstva)
• Član povjerenstva: Adriana Kenđel (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prirodoslovno-matematički fakultet; (Kemijski odsjek); Zagreb
• Datum i država obrane: 2021-07-15, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija

Sažetak

U svrhu analize sterigmatocistina (STC) spektroskopijom površinski pojačanog Ramanovog raspršenja (SERS) pripravljeni su supstrati zlata koji su sadržavali nanočestice dispergirane u suspenziji i imobilizirane na čvrstim nosačima. SERS učinkovitost metalnih supstrata testirana je s rodaminom 6G (R6G). U koloidnim suspenzijama zlata opaženo je intenzivno pojačanje Ramanovog raspršenja R6G nakon pobude zračenjem 785 nm, dok je pri pobudi zračenjem 532 nm spektre zasjenila fluorescencija rodaminske boje. Prisutnost agregirajuće soli u koloidnoj suspenziji nije utjecala na osjetljivost mjerenja R6G. U spektrima STC u koloidu zlata, neovisno o valnoj duljini pobude, nisu opažene vrpce STC, već vrpce metanola u kojem je pripravljena otopina STC, te vrpce citratnih iona i njihovih oksidacijskih/razgradnih produkata zaostalih nakon sinteze na površini nanočestica zlata. Karakteristične vrpce STC vrlo slabog intenziteta uočene su za najviše mjerene koncentracije STC u spektrima koloidnih uzoraka agregiranih amonijevim sulfatom. U spektrima čvrstih supstrata zlata na podlozi od stakla, snimljenim nakon pobude zračenjem 785 nm, dominira fotoluminescencija stakla. Slabo Ramanovo raspršenje R6G na supstratu zlata na staklu uočeno je nakon pobude pri 532 nm. Pojačanje Ramanovog raspršenja na nanočesticama zlata imobiliziranim na podlozi od aluminija nije opaženo niti za R6G niti za STC.

Sažetak (engleski)

In order to analyze sterigmatocystin (STC) by surface-enhanced Raman scattering (SERS) spectroscopy, gold substrates were prepared containing nanoparticles dispersed in suspension and immobilized on solid supports. The SERS efficiency of metal substrates was tested with rhodamine 6G (R6G). In colloidal gold suspensions, an intense enhancement of R6G Raman scattering was observed at excitation of 785 nm, while the spectra were overshadowed by rhodamine dye fluorescence at excitation of 532 nm. The presence of an aggregating salt in the colloid did not affect the sensitivity of the R6G measurements. In the spectra of STC in the gold colloid, regardless of the excitation wavelength, STC bands were not observed, but bands of methanol, in which the STC solution was prepared, and bands of citrate ions and their oxidation/degradation products, which remained on the gold nanoparticles surface after the synthesis. Characteristic STC bands of very low intensity were observed for the highest measured STC concentrations in the spectra of colloidal samples aggregated with ammonium sulfate. The spectra of the solid gold substrates on a glass support, taken at 785 nm excitation, were dominated by photoluminescence of glass. Weak Raman scattering of R6G on the gold substrate on glass was observed after excitation at 532 nm. The enhancement of the Raman scattering on the gold nanoparticles immobilized on an aluminum support was not obtained for either R6G or STC.

• Ključne riječi: čvrsti nosač; koloid; nanočestice zlata; rodamin 6G; SERS; sterigmatocistin
• Ključne riječi (engleski): solid support; colloid; gold nanoparticles; rhodamine 6G; SERS; sterigmatocystin
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:217:380089
• Studijski program: Naziv: Kemija; smjerovi: istraživački; Smjer: istraživački; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra kemije (mag. chem.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup; Datum isteka embarga: 2022-07-15
• Datum i vrijeme pohrane: 2021-09-02 08:37:30