Utjecaj molarne mase polielektrolita na formiranje i svojstva ultra-tankih filmova poli(alilamin-hidroklorida) i poli(akrilne kiseline)

diplomski rad

• Naslov (engleski): Influence of polyelectrolyte molar mass on formation and properties of poly(allylamine hydrochloride)7poly(acrylic acid) ultra-thin films
• Autor: Matej Masjar
• Mentor: Davor Kovačević (mentor)
• Član povjerenstva: Davor Kovačević (predsjednik povjerenstva)
• Član povjerenstva: Željka Soldin (član povjerenstva)
• Član povjerenstva: Adriana Kenđel (član povjerenstva)
• Član povjerenstva: Tajana Begović (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prirodoslovno-matematički fakultet; (Kemijski odsjek); Zagreb
• Datum i država obrane: 2022-09-29, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija

Sažetak

U ovom radu je istražen utjecaj molarne mase polielektrolita na formiranje i svojstva
polielektrolitnog višesloja poli(alilamin-hidroklorida) i poli(akrilne kiseline). U te svrhe
filmovi su pripravljeni s različitim kombinacijama molarnih masa polielektrolita sloj po sloj
metodom na površini silicijeva supstrata pri različitim eksperimentalnim uvjetima kako bi se
utjecalo na konformaciju polimernih lanaca. Elipsometrom je praćena debljina filma tijekom
njegove priprave, a mikroskopom atomskih sila je određena morfologija, hrapavost i poroznost
površine filma. Iz dobivenih podataka utvrđeno je da se povećanjem molarne mase
polielektrolita povećava debljina filma ako je barem jedan polielektrolit u globularnoj
konformaciji. Pokazano je da molarna masa polielektrolita nema značajni utjecaj na debljinu i
hrapavost filma ako su oba polielektrolita u izduženoj konformaciji. Otkrivena su i dva nova
načina priprave ultra-tankih filmova (d ≈ 2 nm) s poli(akrilnom kiselinom) male molarne mase.

Sažetak (engleski)

In this study the influence of the polyelectrolyte molar mass on the formation and properties of
poly(allylamine hydrochloride)/poly(acrylic acid) polyelectrolyte multilayer was investigated.
For these purposes, films were prepared on the silicon substrate using layer by layer method
with different combinations of polyelectrolyte molar masses under different experimental
conditions in order to influence the conformation of the polymer chains. The thickness of the
film was monitored during its preparation with an ellipsometer and the morphology, roughness,
and porosity of the film surface were determined with an atomic force microscope. From
obtained data, it was established that by increasing the polyelectrolyte molar mass, the thickness
of the film increases if at least one polyelectrolyte is in globular conformation. On the other
hand, if both polyelectrolytes are in an elongated conformation, the polyelectrolyte molar mass
has no significant influence on the thickness and roughness of the film. Also, two new ways of
preparation of ultra-thin films (d ≈ 2 nm) were discovered by using poly(acrylic acid) of low
molar mass.

• Ključne riječi: elipsometrija; mikroskopija atomskih sila; molarna masa; polielektrolitni višesloj
• Ključne riječi (engleski): atomic force microscopy; ellipsometry; molar mass; polyelectrolyte multilayer
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:217:529992
• Projekt: Šifra: IPS-2020-01-6126; Naziv: Modulacija polifenolnog profila voća uslijed fizikalnih tretmana nakon branja; Naziv: Modulation of fruit polyphenolic profile by sustainable postharvest physical treatments; Voditelj: Davor Kovačević; Pravna nadležnost: Hrvatska; Financijer: HRZZ; Linija financiranja: IPS
• Studijski program: Naziv: Kemija; smjerovi: istraživački; Smjer: istraživački; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra kemije (mag. chem.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup; Datum isteka embarga: 2024-09-29
• Datum i vrijeme pohrane: 2022-10-25 12:55:22