Karakterizacija nanočestica silicijevog dioksida različitih veličina te njihova modifikacija polielektrolitom

diplomski rad

• Naslov (engleski): Characterisation of silicon dioxide nanoparticles of different sizes and their modification by polyelectrolyte
• Autor: Antun Habajec
• Mentor: Davor Kovačević (mentor)
• Mentor: Juraj Nikolić (komentor)
• Član povjerenstva: Davor Kovačević (predsjednik povjerenstva)
• Član povjerenstva: Ivan Nemet (član povjerenstva)
• Član povjerenstva: Vinko Nemec (član povjerenstva)
• Član povjerenstva: Gordan Horvat (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prirodoslovno-matematički fakultet; (Kemijski odsjek); Zagreb
• Datum i država obrane: 2025-02-11, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija

Sažetak

Nanočestice silicijeva dioksida pokazuju veliki potencijal za primjenu u raznim područjima te je za njihovu primjenu važno razumjeti kako veličina utječe na njihova ostala svojstva. Nadalje, modificiranjem nanočestica adsorpcijom polielektrolita moguće je promijeniti njihova svojstva. Polielektroliti su makromolekule čije podjedinice sadrže ionske ili lako ionizirajuće skupine te ih je moguće adsorbirati na površine suprotnog naboja. U ovome radu istražen je utjecaj veličine nanočestica... Više silicijeva dioksida na njihova svojstva te su korištene čestice promjera od 10 nm do 100 nm. Veličina čestica određena je mikroskopijom atomskih sila te pretražnom elektronskom mikroskopijom. Dinamičkim i elektroforetskim raspršenjem svjetlosti određeni su hidrodinamički promjer i ζ-potencijal nanočestica pri različitim koncentracijama natrijeva klorida. Površinski naboj određen je titracijom nanočestica otopinom polielektrolita. Zatim je na nanočestice adsorbiran poli(N-etil-4-vinilpiridinijev) bromid te je određeno kako maksimalna koncentracija polielektrolita ovisi o veličini čestica. Također su određeni veličina čestica, hidrodinamički promjer te ζ-potencijal i uspoređeni s nemodificiranim česticama. Sakrij dio sažetka

Sažetak (engleski)

Silicon dioxide nanoparticles show great potential for application so it’s important to understand how their size affects their other properties. It is possible to modify nanoparticle properties my adsorbing polyelectrolytes on them. Polyelectrolytes are macromolecules which contain ionic or easily ionisable groups, and they can be adsorbed on oppositely charges surfaces. The influence of silicon dioxide nanoparticle size on their properties was studied for nanoparticles with a... Više diameter of 10 nm to 100 nm. Particle size was determined by atomic force microscopy and scanning electron microscopy. Dynamic and electrophoretic light scattering was used to determine the hydrodynamic radius and ζ-potential of the particles at different concentrations of sodium chloride. Surface charge was determined by titrating nanoparticles with polyelectrolyte. Then, poly(N-ethyl-4-vinylpyridinium) bromide was adsorbed and the dependence of maximum polyelectrolyte concentration on particle diameter was shown. Particle size, hydrodynamic radius and ζ-potential were also determined and compared to unmodified particles. Sakrij dio sažetka

• Ključne riječi: adsorpcija; nanočestice; poli(N-etil-4-vinilpiridinijev) bromid; površinski naboj; silicijev dioksid
• Ključne riječi (engleski): adsorption; nanoparticles; poly(N-ethyl-4-vinylpyridinium) bromide; silicon dioxide; surface charge
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:217:033853
• Projekt: Šifra: IP-2020-02-9571; Naziv: Fizikalna kemija procesa na međupovršini mineral/otopina (poli)elektrolita; Naziv: Physical chemistry of processes at mineral/(poly)electrolyte solution interface; Kratica: POLYMIN2; Voditelj: Tajana Begović; Pravna nadležnost: Hrvatska; Financijer: Hrvatska zaklada za znanost; Linija financiranja: Research Projects
• Studijski program: Naziv: Kemija; smjerovi: Istraživački; Smjer: Istraživački; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: sveučilišni/a magistar/magistra kemije (univ. mag. chem.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Rad dostupan nakon; Datum isteka embarga: 2026-02-11
• Datum i vrijeme pohrane: 2025-02-14 13:44:55