Temperature dependence of microstructure in Zn-Al alloys
Fizika A, 8 (1999), 3; 173-182. urn:nbn:hr:217:974557
Popović, Stanko; Gržeta, Biserka; Hanžek, Branko; Hajster, Snježana

Citirajte ovaj rad

Popović, S., Gržeta, B., Hanžek, B. i Hajster, S. (1999). Temperature dependence of microstructure in Zn-Al alloys. Fizika A, 8. (3), 173-182. Preuzeto s https://urn.nsk.hr/urn:nbn:hr:217:974557

Popović, Stanko, et al. "Temperature dependence of microstructure in Zn-Al alloys." Fizika A, vol. 8, br. 3, 1999, str. 173-182. https://urn.nsk.hr/urn:nbn:hr:217:974557

Popović, Stanko, Biserka Gržeta, Branko Hanžek i Snježana Hajster. "Temperature dependence of microstructure in Zn-Al alloys." Fizika A 8, br. 3 (1999): 173-182. https://urn.nsk.hr/urn:nbn:hr:217:974557

Popović, S., et al. (1999) 'Temperature dependence of microstructure in Zn-Al alloys', Fizika A, 8(3), str. 173-182. Preuzeto s: https://urn.nsk.hr/urn:nbn:hr:217:974557 (Datum pristupa: 15.11.2024.)

Popović S, Gržeta B, Hanžek B, Hajster S. Temperature dependence of microstructure in Zn-Al alloys. Fizika A [Internet]. 1999. [pristupljeno 15.11.2024.];8(3):173-182. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:217:974557

S. Popović, B. Gržeta, B. Hanžek i S. Hajster, "Temperature dependence of microstructure in Zn-Al alloys", Fizika A, vol. 8, br. 3, str. 173-182, 1999. [Online]. Dostupno na: https://urn.nsk.hr/urn:nbn:hr:217:974557. [Citirano: 15.11.2024.]

Za citiranje koristite ovu mrežnu adresu: https://urn.nsk.hr/urn:nbn:hr:217:974557
Prijavite se u repozitorij kako biste mogli spremiti objekt u svoju listu.
Podaci o radu
Naslov (engleski)Temperature dependence of microstructure in Zn-Al alloys
AutorStanko Popović
AutorBiserka Gržeta
AutorBranko Hanžek
AutorSnježana Hajster
Autorova ustanovaSveučilište u Zagrebu
Prirodoslovno-matematički fakultet
(Fizički odsjek)
Znanstveno / umjetničko
područje, polje i grana		PRIRODNE ZNANOSTI
Fizika
Sažetak (engleski)
The temperature dependence of microstructure in Zn-Al alloys, transferred to the equilibrium state by quenching from the solid solution temperature, T_SS, to room temperature (RT) and prolonged ageing at RT, was studied in situ by X-ray powder diffraction. Instead of the phase transitions expected according to the phase diagram, namely α (M/β) + β → α' + α(M/α') → α_SS for the alloy with 54 at% Zn and α(M/β) + β → α'+β → α_SS for the alloy with 62 at% Zn, the following sequence was observed for both alloys: α(M/β) + β → α' + β+ α(M/α', β) → α'+β → α_SS. In the cooling run, a temperature hysteresis in reversal phase transitions was observed. During a repeated heating, the microstructure depended on the previous thermal treatment of the alloys.
Ključne riječi (engleski)
Jezikengleski
Vrsta publikacijeZnanstveni rad - Izvorni znanstveni rad
Status objaveObjavljen
Vrsta recenzijeRecenziran
Verzija publikacijeObjavljena verzija rada (izdavačev PDF)
Naslov časopisaFizika A
Brojčani podacivol. 8, br. 3, str. 173-182
p-ISSN1330-0008
URN:NBNurn:nbn:hr:217:974557
Datum objave publikacije1999
URL dokumentahttp://fizika.hfd.hr/fizika_a/av99/a8p173.htm
Vrsta resursaTekst
Prava pristupaOtvoreni pristup
Uvjeti korištenjaIkona licence Zaštićeno autorskim pravom.
Datum i vrijeme pohrane2019-10-09 12:24:09