Sinteza i karakterizacija šupljih nanosfera poli(alilamina) i poli(akrilne kiseline)

diplomski rad

• Naslov (engleski): Synthesis and characterization of hollow nanospheres of poly(allylamine) and poly(acrylic acid)
• Autor: Nikolina Peranić
• Mentor: Davor Kovačević (mentor)
• Član povjerenstva: Davor Kovačević (predsjednik povjerenstva)
• Član povjerenstva: Željka Soldin (član povjerenstva)
• Član povjerenstva: Adriana Kenđel (član povjerenstva)
• Član povjerenstva: Tajana Begović (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prirodoslovno-matematički fakultet; (Kemijski odsjek); Zagreb
• Datum i država obrane: 2020-12-22, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija

Sažetak

Naizmjeničnom adsorpcijom pozitivno i negativno nabijenih polielektrolita na površinu supstrata (npr. koloidne čestice) nastaju tanki filmovi zvani polielektrolitni višeslojevi. U slučaju adsorpcije na sferične čestice moguće je (uklanjanjem supstrata) prirediti šuplje sfere mikrometarskih ali i nanometarskih dimenzija koje imaju različita fizikalno-kemijska svojstva. Zbog velikog broja dostupnih polimernih spojeva navedeni sustavi nalaze svoju primjenu u područjima biomedicine, katalize i sinteze funkcionaliziranih nanomaterijala. U ovom radu uspješno su sintetizirane šuplje nanosfere slabih polielektrolita, poli(alilamina) i poli(akrilne kiseline), pri čemu su kao supstrati korištene čestice hidroksiapatita. Nastanak polielektrolitnog višesloja na koloidnim česticama praćen je mjerenjem elektroforetske pokretljivosti čestica, a uklanjanje supstrata provedeno je otapanjem u prisustvu klorovodične kiseline. Metodom dinamičkog raspršenja svjetlosti određen je efektivni hidrodinamički promjer dobivenih polielektrolitnih kapsula, a mikroskopijom atomskih sila i skenirajućom elektronskom mikroskopijom dobivene su informacije o morfologiji i veličini nanosfera. Infracrvenom spektroskopijom i energijski disperzijskom rendgenskom analizom potvrđeno je uklanjanje supstrata.

Sažetak (engleski)

By alternating adsorption of positively and negatively charged polyelectrolytes on the surface of the substrate (e.g. colloidal particles), thin films called polyelectrolyte multilayers are formed. In the case of adsorption on spherical nanoparticles it is possible (by removing the substrate) to prepare hollow spheres of micrometer and nanometer dimensions with various physico-chemical properties. Due to the large number of available polymeric compounds, these systems find their application in the fields of biomedicine, catalysis and functionalized nanomaterial synthesis. In this study, hollow nanospheres of weak polyelectrolytes, poly(allylamine) and poly(acrylic acid) were successfully synthesized, using hydroxyapatite particles as substrates. The formation of the polyelectrolyte multilayer on colloidal particles was monitored by measuring the electrophoretic mobility of the particles, and the removal of the substrate was obtained by dissolution in the presence of hydrochloric acid. The effective hydrodynamic diameter of the obtained polyelectrolyte capsules was determined by the method of dynamic light scattering, while information on the morphology and size of nanospheres was obtained by atomic force microscopy and scanning electron microscopy. Infrared spectroscopy and energy dispersion X-ray analysis confirmed the removal of the substrate.

• Ključne riječi: hidroksiapatit; nanosfere; poli(akrilna kiselina); poli(alilamin); polielektrolitni višeslojevi
• Ključne riječi (engleski): hydroxyapatite; nanospheres; poly(acrylic acid); poly(allylamine); polyelectrolyte multilayers; solubility
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:217:533356
• Studijski program: Naziv: Kemija; smjerovi: istraživački; Smjer: istraživački; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra kemije (mag. chem.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup; Datum isteka embarga: 2022-12-22
• Datum i vrijeme pohrane: 2021-02-16 12:48:59