Sinteza i karakterizacija nanočestica različitih morfologija

diplomski rad

• Naslov (engleski): Synthesis and characterization of nanoparticles of different morphologies
• Autor: Karla Gotić
• Mentor: Davor Kovačević (mentor)
• Član povjerenstva: Davor Kovačević (predsjednik povjerenstva)
• Član povjerenstva: Marijana Đaković (član povjerenstva)
• Član povjerenstva: Iva Juranović Cindrić (član povjerenstva)
• Član povjerenstva: Branimir Bertoša (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prirodoslovno-matematički fakultet; (Kemijski odsjek); Zagreb
• Datum i država obrane: 2019-12-13, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija

Sažetak

U sklopu ovog rada istraženo je nekoliko morfološki različitih nanočestica kako bi se
pronašao potencijalan materijal za izolaciju jednog od najopasnijih radioaktivnijih kationa
cezija iz nuklearnog otpada. Sintetizirana su tri različita tipa čestica cerijeva(IV) oksida –
nanosfere te nanokockice dviju različitih veličina. Uz njih su dodatno okarakterizirane
nanocjevčice titanijeva(IV) oksida. Metodom difrakcije rendgenskog zračenja na praškastom
uzorku potvrđen je sastav te je procijenjena veličina čestica dok je transmisijskom
elektronskom mikroskopijom određena veličina te opisana morfologija čestica. BET analizom
je određena specifična površina svih čestica, a metodom elektroforeze je praćena pokretljivost
čestica u vodenim suspenzijama. Određen je i utjecaj dva alkalijska kationa Na+ i Cs+ na
pokretljivost te na izoelektričnu točku svih tipova čestica. Konačno su svi rezultati uspoređeni
te su se nanocjevčice TiO2 pokazale kao potencijalno povoljan materijal za opis adsorpcije
cezijevog kationa.

Sažetak (engleski)

In this diploma thesis several morphologically different types of nanoparticles were
investigated to find a potential material for isolation of one of the most dangerous radioactive
cations caesium from nuclear waste. Three different types of cerium(IV) oxide nanoparticles
were synthesized and characterised - nanospheres and nanocubes in two different sizes.
Additionally, nanotubes of titanium(IV) oxide were characterised. Using X-ray powder
diffraction method composition was determined and the size of the particles was estimated.
The size and morphology of the nanoparticles was confirmed using TEM; while BET analysis
was used to determine specific nanoparticle surface. Mobility was monitored using
electrophoresis in water suspensions. Additionally, the effect of two alkali cations (Na+ and
Cs+) on mobility and on the isoelectric point has been studied. Finally, all of the results were
compared, and it was established that TiO2 nanotubes are the best material for the assessment
of caesium cation adsorption.

• Ključne riječi: cerijev(IV) oksid; cezij; elektroforetsko raspršenje svjetlosti; izoelektrična točka; nanočestice; TEM; titanijev(IV) oksid
• Ključne riječi (engleski): cerium(IV) oxide; caesium; electrophoretic light scattering; isoelectric point; TEM; titanium(IV) oxide.
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:217:472138
• Studijski program: Naziv: Kemija; smjerovi: istraživački; Smjer: istraživački; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra kemije (mag. chem.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup; Datum isteka embarga: 2021-12-13
• Datum i vrijeme pohrane: 2020-01-10 14:02:21