Površinski pojačano Ramanovo raspršenje odabranih organskih boja na nanočesticama srebra I zlata

diplomski rad

• Naslov (engleski): Surface-enhanced Raman scattering of selected organic dyes on silver and gold nanoparticles
• Autor: Izabela Đurasović
• Mentor: Adriana Kenđel (mentor)
• Član povjerenstva: Adriana Kenđel (predsjednik povjerenstva)
• Član povjerenstva: Biserka Prugovečki (član povjerenstva)
• Član povjerenstva: Ivana Biljan (član povjerenstva)
• Član povjerenstva: Snežana Miljanić (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prirodoslovno-matematički fakultet; (Kemijski odsjek); Zagreb
• Datum i država obrane: 2021-09-29, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija

Sažetak

Učinkovitost površinski pojačanog Ramanova raspršenja (SERS) nanočestica srebra i zlata
dispergiranih u svježe pripravljenim i koncentriranim koloidima te imobiliziranih na staklu
tretiranom s fluorovodičnom kiselinom i staklenom filter-papiru istraživana je pomoću metilenskog
modrila (MetB) i rodamina B (RB) pri pobudama 532 i 785 nm. Koncentrirane koloidne suspenzije
jače pojačavaju raspršenje zračenja boja u odnosu na svježe pripravljene koloide. U koncentriranom
koloidu zlata pri pobudi 785 nm opažene spektralne promjene upućuju na drugačiju orijentaciju
molekula MetB na površini zlata, u odnosu na koloid srebra. Atom sumpora iz fenotiazinskog
sustava boje tvori kemijsku vezu sa zlatom, dok su u koloidu srebra molekule MetB vezane na
supstrat preko atoma dušika fenotiazina. Kod svih korištenih supstrata pobuda pri 785 nm rezultira
intenzivnim vrpcama MetB i RB, dok pobuda pri 532 nm daje vrpce slabijeg intenziteta za MetB,
a vrpce RB zasjenjuje široka vrpca fluorescencije. U odnosu na koloidne suspenzije, nanočestice
srebra i zlata imobilizirane na čvrstim podlogama nisu se pokazale reproducibilnim supstratima
zbog neravnomjerne raspodjele nanočestica metala na površini supstrata.

Sažetak (engleski)

Efficiency of surface-enhanced Raman scattering (SERS) of silver and gold nanoparticles dispersed
in freshly prepared and concentrated colloids, and immobilized on hydrofluoric acid-treated glass
and glass-fiber filter paper was investigated using methylene blue (MetB) and rhodamine B (RB)
at excitation of 532 and 785 nm. Concentrated colloidal suspensions intensified the scattering of
dye radiation, compared to freshly prepared colloids. In the concentrated gold colloid at 785 nm,
observed spectral changes indicated a different orientation of MetB molecules on metal surface,
compared to the silver colloid. The sulfur atom from phenothiazine created a chemical bond with
gold, while MetB molecules in the silver colloid were bonded to the substrate via phenothiazine
nitrogen atom. For all used substrates, the excitation at 785 nm resulted in intense MetB and RB
bands, while excitation at 532 nm yielded lower-intensity bands for MetB, and a wide fluorescence
band that overlapped RB bands. Metal colloidal suspensions were more reproducible substrates
than the solid substrates, due to the uneven distribution of nanoparticles on the solid substrates.

• Ključne riječi: metilensko modrilo; nanočestice; rodamin B; SERS; srebro; zlato
• Ključne riječi (engleski): gold; methylene blue; nanoparticles; rhodamine B; SERS; silver
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:217:548698
• Studijski program: Naziv: Kemija; smjerovi: istraživački; Smjer: istraživački; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra kemije (mag. chem.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup; Datum isteka embarga: 2023-09-29
• Datum i vrijeme pohrane: 2021-10-18 10:28:12