Polielektrolitni višesloj kitozan/poli(akrilna kiselina): priprava, bubrenje i samozacjeljivanje nanofilma

diplomski rad

• Naslov (engleski): Chitosan/poly(acrylic acid) polyelectrolyte multilayer: preparation, swelling and self-healing of a nanofilm
• Autor: Ivan Živković
• Mentor: Davor Kovačević (mentor)
• Mentor: Damir Hasenay (mentor)
• Član povjerenstva: Davor Kovačević (predsjednik povjerenstva)
• Član povjerenstva: Željka Soldin (član povjerenstva)
• Član povjerenstva: Ivana Biljan (član povjerenstva)
• Član povjerenstva: Tajana Begović (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prirodoslovno-matematički fakultet; (Kemijski odsjek); Zagreb
• Datum i država obrane: 2022-02-23, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija

Sažetak

Uspješno su pripravljeni višeslojevi kitozan/poli(akrilna kiselina) s različitim brojem slojeva na
površini supstrata od silicija. Elipsometrijskim mjerenjima dokazan je eksponencijalni rast
debljine filma s brojem adsorbiranih slojeva i ireverzibilnost procesa bubrenja filma. Ni jedan
od pripravljenih polielektrolitnih višeslojeva nije pokazao značajniju promjenu debljine s
promjenom relativne vlažnosti atmosfere kojoj su bili izloženi. Međutim, pomalo neočekivano
većini uzoraka se smanjila debljina prilikom izlaganja visokoj relativnoj vlažnosti. Kako bi se
detaljnije istražio ovaj efekt, mikroskopom atomskih sila snimljena je površina desetoslojnog
filma prije i nakon izlaganja nanofilma visokoj relativnoj vlažnosti. Na snimkama je uočeno da
se gustoća otoka koje formiraju polielektroliti na površini supstrata smanjila nakon ovakvog
tretmana višesloja što bi moglo biti zbog reorganizacije polielektrolitnih lanaca. Na kraju je
digitalnim optičkim mikroskopom praćeno samozacjeljivanje mehanički oštećenog filma od 60
slojeva. Film je neznatno zacijelio pri visokoj relativnoj vlažnosti, dok je uporabom
deionizirane vode na oštećenju došlo do značajnijeg samozacjeljivanja.

Sažetak (engleski)

Chitosan/poly(acrylic acid) multilayers with different numbers of layers were successfully
prepared on the surface of a silicon substrate. Ellipsometric measurements have shown the
exponential increase in the thickness of the multilayer with the increasing number of layers and
the irreversibility of the swelling process. None of the prepared films showed an increase in
thickness by changing the relative humidity they were exposed to. Unexpectedly, the films have
shown a large decrease in their thickness when they were exposed to high relative humidity. In
order to investigate this phenomenon, a surface of the 10-layered film was imaged by atomic
force microscope before and after exposure of the nanofilm to high relative humidity.
Microscopy scans have shown a decrease in the density of polyelectrolyte islands on a substrate
surface caused by this treatment. The reason for that is probably the reorganization of
polyelectrolyte chains. Self-healing of the mechanically damaged film of 60 layers was
monitored with a digital optical microscope. At high relative humidity, the film heals slightly,
while the use of deionized water on the damaged region caused much more pronounced selfhealing.

• Ključne riječi: bubrenje; polielektrolitni višesloj; relativna vlažnost; samozacjeljivanje
• Ključne riječi (engleski): polyelectrolyte multilayer; relative humidity; self-healing; swelling
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:217:370232
• Projekt: Šifra: IPS-2020-01-6126; Naziv: Modulacija polifenolnog profila voća uslijed fizikalnih tretmana nakon branja; Naziv: Modulation of fruit polyphenolic profile by sustainable postharvest physical treatments; Voditelj: Davor Kovačević; Pravna nadležnost: Hrvatska; Financijer: HRZZ; Linija financiranja: IPS
• Studijski program: Naziv: Kemija; smjerovi: istraživački; Smjer: istraživački; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra kemije (mag. chem.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup; Datum isteka embarga: 2024-02-23
• Datum i vrijeme pohrane: 2022-02-28 12:46:27