Ispitivanje utjecaja modifikacije nanočestica željeza s 1,5-difenilkarbazidom pri sorpciji kroma iz vodenih otopina

diplomski rad

• Naslov (engleski): Investigation of effects of 1,5-diphenylcarbazide modifyed iron nanoparticles on chromium sorption from aquoeous solutions
• Autor: Valentina Starešinčić
• Mentor: Sanda Rončević (mentor)
• Član povjerenstva: Sanda Rončević (predsjednik povjerenstva)
• Član povjerenstva: Ivana Biljan (član povjerenstva)
• Član povjerenstva: Biserka Prugovečki (član povjerenstva)
• Član povjerenstva: Iva Juranović Cindrić (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prirodoslovno-matematički fakultet; (Kemijski odsjek); Zagreb
• Datum i država obrane: 2019-09-24, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija

Sažetak

U radu je ispitano uklanjanje kroma(VI) iz modelnih vodenih otopina pomoću neutralnih i modificiranih nanočestica željeza. Pri tome su sintetizirane neutralne nanočestice željeza redukcijom iona željeza(III) iz vodene otopine natrijevim borhidridom. Nanočestice su modificirane s 1,5difenilkarbazidom u različitim molarnim omjerima liganda i željeza: 1:2, 1:1, 3:2 i 2:1. Sintetizirane nanočestice okarakterizirane su metodama strukturne analize: infracrvenom spektroskopijom (FT-IR), pretražnom elektronskom mikroskopijom (SEM) i difrakcijom rendgenskog zračenja u polikristalnom uzorku (XRD). Rezultati su pokazali da se čestice sastoje od magnetita i α-željeza. Nakon funkcionalizacije dolazi do promjene dendritične strukture nanočestica u aglomerate s manjim srednjim promjerom sfera. Preliminarna ispitivanja učinkovitosti sorpcije kroma(VI) provedena su UV/Vis spektrofotometrijom. Uklanjanje kroma iz modelnih vodenih otopina nakon sorpcije na modificiranim i neutralnim nanočesticama praćeno je emisijskom spektrometrijom uz induktivno spregnutu plazmu (ICP-AES). Udio uklonjenog kroma varira između 79 % i 91 %. Rezultati su pokazali da je učinkovitost uklanjanja kroma(VI) izraženija uz dodatak 1,5-difenilkarbazida.

Sažetak (engleski)

Removal of chromium(VI) from model aqueous solution using bare and modified iron nanoparticles was investigated. Zero-valent iron nanoparticles were synthesized by sodium borohydride reduction of iron(III) ions in water solution. Nanoparticles were functionalized by addition of 1,5diphenylcarbazide in different molar ratios of ligand and iron (1:1; 1:2; 3:2; 2:1). Synthesized nanoparticles were characterized by structural analysis methods such as infrared spectroscopy (FT-IR), scanning electron microscopy (SEM) and X-ray diffraction of polycrystals (XRD). It was found that particles consisted of magnetite and α-Fe. Dendritic structure of bare particles was changed after functionalization into agglomerates along with decrease of average diameter of spheres. Preliminary test of chromium removal efficiency was performed using UV/VIS spectrophotometry. Removal of chromium from water solutions was analysed using inductively coupled atomic emission spectrometry (ICP-AES). Mass fraction of removed chromium was varied between 79 % - 91%. The obtained results showed that efficiency of chromium(VI) removal is pronounced with addition of 1,5-diphenylcarbazide.

• Ključne riječi: 1; 5-difenilkarbazid; ICP-AES; karakterizacija; krom; nanočestice; željezo
• Ključne riječi (engleski): 1; 5-diphenylcarbazide; characterization; chromium; ICP-AES; iron; nanoparticles
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:217:645045
• Studijski program: Naziv: Kemija; smjerovi: istraživački; Smjer: istraživački; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra kemije (mag. chem.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup; Datum isteka embarga: 2021-09-24
• Datum i vrijeme pohrane: 2019-09-27 08:16:09