Novi pogledi na mehanizme električnoga prijenosa u ionsko-polaronskim staklima

disertacija

• Naslov (engleski): New insights into electrical transport mechanisms in ion-polaron glasses
• Autor: Juraj Nikolić
• Mentor: Andrea Moguš-Milanković (mentor)
• Član povjerenstva: Višnja Vrdoljak (predsjednik povjerenstva)
• Član povjerenstva: Ana Šantić (član povjerenstva)
• Član povjerenstva: Krešimir Molčanov (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prirodoslovno-matematički fakultet; (Kemijski odsjek); Zagreb
• Datum i država obrane: 2020-07-09, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija
• Univerzalna decimalna klasifikacija (UDC): 54 - Kemija. Kristalografija. Mineralogija

Sažetak

U ovoj doktorskoj disertaciji istražen je utjecaj zamjene Li2O, Na2O i Ag2O s WO3 odnosno MoO3 na strukturu, električna/dielektrična svojstva i promjenu mehanizama električne vodljivosti, ionske i polaronske, u cink fosfatnim stakalima. Strukturne su promjene istražene Ramanovom spektroskopijom, a (di)električna svojstva impedancijskom spektroskopijom. Strukturna su istraživanja pokazala da dodatkom WO3 dolazi do ugradnje WO6 oktaedarskih jedinica u staklo te do pojave klasteriranja, dok ugradnjom MoO3 nastaje trodimenzijska molibdensko-fosfatna strukturna mreža bez klasteriranja molibdenskih jedinica. Rezultati impedancijske spektroskopije pokazali su da dodatkom WO3 u stakla dolazi do pojave minimuma vrijednosti električne provodnosti. S druge strane, dodatkom MoO3 dolazi do blagog rasta (Li2O i Na2O serije) ili pada (Ag2O serija) vrijednosti provodnosti uz porast provodnosti tek za 60Mo polaronsko staklo. Analizom kompleksnih impedancijskih ravnina i postupkom skaliranja spektara električne provodnosti utvrđena je prisutnost ionskog i polaronskog mehanizma vodljivosti u staklima u koje je dodan WO3.

Sažetak (engleski)

This thesis studies structural and electrical changes which occur due to replacement of Li2O, Na2O and Ag2O by WO3 and MoO3 in zinc phosphate glasses. This study focuses on mechanisms of electrical conductivity, ionic and polaronic, as a result of the oxide replacement. Raman spectroscopy was used to determine the glass structure whereas electrical properties were investigated using impedance spectrosopy. Structural studies have revealed that adding WO3 to phosphate network causes incorporation of WO6 units and formation of clusters in phosphate network, while addition of MoO3 forms three-dimensional molybdenum-phosphate glass network without clustering of molybdenum units. Results of impedance spectroscopy have shown that addition of WO3 into the phosphate network causes a minimum in electrical conductivity while adding MoO3 causes minor increase (Li2O and Na2O series) or a decrease (Ag2O series) in electrical conductivity, showing increase only for polaronic 60Mo glass. Presence of both ionic and polaronic mechanisms of electrical conductivity in tungstate glasses was confirmed by analysis of complex impedance planes and scaling of conductivity spectra.

• Ključne riječi: fosfatna stakla; električna svojstva; struktura; impedancijska spektroskopija
• Ključne riječi (engleski): phosphate glasses; electrical properties; structure; impedance spectroscopy
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:217:577555
• Datum promocije: 2020
• Studijski program: Naziv: Kemija; Vrsta studija: sveučilišni; Stupanj studija: poslijediplomski doktorski; Akademski / stručni naziv: doktor/doktorica znanosti, područje prirodnih znanosti, polje kemija (dr. sc.)
• Vrsta resursa: Tekst
• Opseg: 130 str. ; 30 cm
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Otvoreni pristup
• Datum i vrijeme pohrane: 2020-07-17 09:08:52