Električna i termička svojstva fleksibilnih kristala koordinacijskih polimera bakrovih(II) halogenida s 3-nitropiridinom

diplomski rad

• Naslov (engleski): Electrical and thermal properties of flexible crystals of coordination polymers of copper(II) halogenides with 3-nitropyridine
• Autor: Lea Čolakić
• Mentor: Marijana Đaković (mentor)
• Mentor: Ana Šantić (mentor)
• Član povjerenstva: Marijana Đaković (predsjednik povjerenstva)
• Član povjerenstva: Đani Škalamera (član povjerenstva)
• Član povjerenstva: Iva Juranović Cindrić (član povjerenstva)
• Član povjerenstva: Dominik Cinčić (član povjerenstva)
• Ustanova koja je dodijelila akademski / stručni stupanj: Sveučilište u Zagrebu; Prirodoslovno-matematički fakultet; (Kemijski odsjek); Zagreb
• Datum i država obrane: 2022-11-14, Hrvatska
• Znanstveno / umjetničko područje, polje i grana: PRIRODNE ZNANOSTI; Kemija

Sažetak

U okviru ovog diplomskog rada sintetizirani su koordinacijski polimeri bakrovih(II) halogenida
s 3-nitropiridinom klasičnom otopinskim sintezom i metodom tekućinske difuzije. Priređeni
spojevi okarakterizirani su infracrvenom spektroskopijom, metodama termičke analize i
difrakcijom rendgenskog zračenja na polikristalnom uzorku, dok im je molekulska i kristalna
struktura otprije poznata. Igličasti kristali priređenih spojeva pokazali su se prilagodljivima na
primjenu vanjskog mehaničkog podražaja uslijed kojeg daju elastičan odziv koji je i
kvantificiran. Jediničnim kristalima pripravljenih spojeva dodatno su proučena termička
svojstva te fleksibilni odziv na primjenu vanjskog toplinskog podražaja pomoću mikroskopije
s grijaćom pločom. Opaženi fleksibilni odzivi korelirani su s jakošću i usmjerenošću
međumolekulskih interakcija ostvarenih u kristalnim strukturama priređenih spojeva. Uz to,
kristalima su proučena i električna svojstva pri različitim temperaturama koristeći
impedancijsku spektroskopiju, kao prvi korak u potencijalnoj primjeni ovih fleksibilnih
kristalnih materijala.

Sažetak (engleski)

Within the scope of this thesis, coordination polymers of copper(II) halogenides with 3-
nitropiridine were prepared via classical solution synthesis and layering technique. The
prepared compounds were characterized by infrared spectroscopy, thermal methods and powder
X-ray diffraction, while their molecular and crystal structures have already been known. The
needle-like crystals of the prepared compounds have proven adaptable to the applied
mechanical stimuli, which resulted in elastic responses that have been quantified. Thermal
properties of prepared compounds were additionally studied by examining the flexible response
to the application of external thermal stimuli using hot-stage microscopy. The observed flexible
responses were correlated with the strength and direction of intermolecular interactions
achieved in the crystal structures of the prepared compounds. In addition, temperature
dependance of electrical properties was analyzed using impedance spectroscopy, as the first
step in the potential application of these flexible crystalline materials.

• Ključne riječi: : 3-nitropiridin; bakar(II); fleksibilni kristali; impedancijska spektroskopija; koordinacijski polimeri; kristalno inženjerstvo; mehanička svojstva
• Ključne riječi (engleski): 3-nitropyridine; coordination polymers; copper(II); crystal engineering; flexible crystals; impedance spectroscopy; mechanical properties
• Jezik: hrvatski
• URN:NBN: urn:nbn:hr:217:196423
• Projekt: Šifra: IP-2019-04-1242; Naziv: Od oblika do funkcije: Fleksibilni kristalni materijali s kontroliranim mehaničkim odzivom; Naziv: From form to function: Mechanically flexible crystalline materials with controllable responses; Kratica: FlexibleCrystals; Voditelj: Marijana Đaković; Pravna nadležnost: Hrvatska; Financijer: HRZZ; Linija financiranja: IP
• Studijski program: Naziv: Kemija; smjerovi: istraživački; Smjer: istraživački; Vrsta studija: sveučilišni; Stupanj studija: diplomski; Akademski / stručni naziv: magistar/magistra kemije (mag. chem.)
• Vrsta resursa: Tekst
• Način izrade datoteke: Izvorno digitalna
• Prava pristupa: Rad dostupan nakon; Datum isteka embarga: 2024-11-14
• Datum i vrijeme pohrane: 2022-11-16 11:52:35